| Product |
MgO(%) |
Cr2O3(%) |
SiO2(%) |
A.P(%) |
B.D(gm/cm3) |
C.C.S(kg/cm2) |
RUL Ta (°C) |
Primary Raw Material |
Application area |
| VRPL VRPLD-I |
60 |
15 |
6.5 |
22 |
2.90 |
250 |
1600 |
Dead Burnt Magnesia and Chromite |
DENSE MAGNESIA CHROME for general applications |
| VRPL VRPLD-II |
65 |
12 |
5.0 |
20 |
2.90 |
300 |
1620 |
Dead Burnt Magnesia and Chromite |
| VRPL VRPLD-III |
70 |
10 |
4.0 |
20 |
2.95 |
350 |
1650 |
Dead Burnt Magnesia and Chromite |
| VRPL DBMC-I |
65 |
12 |
3.0 |
18 |
2.95 |
350 |
1650 |
Magnesia-Chrome Co-Clinker,Fused Magnesia and Chromite |
DIRECT BONDED MAGNESIA CHROME for non-ferrous industry |
| VRPL DBMC-II |
70 |
10 |
2.5 |
18 |
3.00 |
400 |
1700 |
Magnesia-Chrome Co-Clinker, Fused Magnesia and Chromite |
| VRPL DBMC-SPL |
65 |
18 |
1.0 |
18 |
3.10 |
400 |
1700 |
Magnesia-Chrome Co-Clinker, Fused Magnesia and Chromite |
| VRPL DBCM-SPL |
50 |
25 |
1.0 |
17 |
3.15 |
400 |
1700 |
Chrome-Magnesia Co-Clinker,Fused Magnesia and Chromite |
| VRPL DBMC-III |
75 |
8 |
2.0 |
18 |
3.05 |
400 |
1700 |
Magnesia-Chrome Co-Clinker, Fused Magnesia and Chromite |
DIRECT BONDED MAGNESIA CHROME for cement industry |
|
|
|
|
|
|
|
|
|
|
|
| Product |
MgO(%) |
Cr2O3(%) |
A.P (%) |
B.D(gm/cm3) |
C.C.S(kg/cm2) |
RUL Ta (°C) |
Primary Raw Material |
Application area |
| VRPL CMN |
35.0 |
18.0 |
25 |
2.85 |
200 |
1550 |
Dead Burnt Magnesia and Chromite |
DENSE CHROME MAGNESIA for general applications |
| VRPL CMN R |
40 |
30 |
21 |
2.90 |
400 |
1550 |
Dead Burnt Magnesia and Chromite |
DENSE CHROME MAGNESIA for reheating furnace hearth |
|
|
|
|
|
|
|
|
|
|
|
| Product |
MgO(%) |
SiO2(%) |
A.P (%) |
B.D(gm/cm3) |
C.C.S(kg/cm2) |
RUL Ta (°C) |
Primary Raw Material |
Application area |
| VRPL MGN |
85 |
6.5 |
22 |
2.85 |
350 |
1550 |
Dead Burnt Magnesia |
MAGNESITE for EAF,Hot Metal Mixer and general apllications |
| VRPL MGD-I |
89 |
5.5 |
20 |
2.88 |
450 |
1580 |
Dead Burnt Magnesia |
| VRPL MGD-II |
91 |
4.5 |
18 |
2.90 |
600 |
1600 |
Dead Burnt Magnesia |
| VRPL MGD-III |
92 |
4.0 |
18 |
2.90 |
600 |
1620 |
Dead Burnt Magnesia |
|
|
|
|
|
|
|
|
|
|
|
| Product |
MgO(%) |
SiO2(%) |
Fe2O3(%) |
A.P (%) |
B.D(gm/cm3) |
C.C.S(kg/cm2) |
RUL Ta (°C) |
Primary Raw Material |
Application area |
| VRPL MGIS-I |
95 |
2.0 |
1.0 |
18 |
2.92 |
600 |
1650 |
Sea-Water Magnesia and Dead Burnt Magnesia |
LOW-IRON MAGNESITE for Glass Industry and special applications |
| VRPL MGIS-II |
96 |
|
0.8 |
18.0 |
2.95 |
600 |
1700 |
Sea-Water Magnesia and Dead Burnt Magnesia |
| VRPL MGIS-III |
97 |
|
0.6 |
18.0 |
2.95 |
600 |
1700 |
Fused Magnesia and Dead Burnt Magnesia |
| VRPL MGIS-IV |
97.5 |
|
0.4 |
17.0 |
2.98 |
600 |
1700 |
Fused Magnesia and Dead Burnt Magnesia |